--- title: "Rebound hammer test" subject: "Concrete Technology and Masonry Structure" chapter: 5 key: "semester_5/concrete_technology_and_masonry_structure:rebound-hammer-test" source: https://www.bctengineer.com/q/semester_5/concrete_technology_and_masonry_structure/rebound-hammer-test site: BCT Engineering --- # Rebound hammer test Concrete Technology and Masonry Structure · Chapter 5: Testing of concrete and quality control - Asked in: 2078 Bhadra, 4 marks - Video: [Rebound Hammer Test on Concrete – Principle, Procedure](https://www.youtube.com/watch?v=pnaS7zKBG5I) — Civil Technology - Answer checked by Claude Sonnet 5.5 on 2026-10-14 - Page: https://www.bctengineer.com/q/semester_5/concrete_technology_and_masonry_structure/rebound-hammer-test - Whole chapter: https://www.bctengineer.com/md/semester_5/concrete_technology_and_masonry_structure/chapter-5 ## Question Explain the non-destructive test by rebound hammer. ## Short answer The rebound hammer test measures surface hardness by striking concrete with a spring-loaded mass; the rebound number (R) on a scale of 10–100 correlates to compressive strength via a calibration curve. Take at least 12 readings on a smooth, dry surface, reject outliers >6 units from mean, and average the rest. Accuracy is ±15–25%, and it tests only about 30 mm depth. ## Answer #### Rebound hammer (Schmidt hammer) test (IS 13311 Part 2) **Principle:** a spring-loaded mass strikes the concrete surface through a plunger. The rebound of the mass, read as the **rebound number** $R$ on a scale of 10 to 100, depends on the surface hardness, which is related to strength. **Procedure** 1. Select a smooth, clean, dry surface of a structural member at least 100 mm thick; grind off plaster, loose scale and rough texture. 2. Hold the hammer at right angles to the surface (if it is held horizontal, or vertically up or down, an orientation correction is needed), push the plunger until the mass is released, and read the rebound number. 3. Take at least **12 readings** at spots 20 to 50 mm apart; reject readings that differ from the mean by more than 6 units, and average the rest. 4. Read the compressive strength from the manufacturer's calibration curve (for the position of the hammer), which should preferably be made from cubes of the same concrete. **Precautions:** avoid edges, honeycombed and wet surfaces, and spots over reinforcement; check the instrument on the test anvil. **Limits:** it tests only the surface (about 30 mm deep), so it is affected by carbonation, moisture, surface finish, type of aggregate and cement, and age. The accuracy of strength is about ±15 to 25%. It is useful for comparing uniformity and for choosing places for coring or UPV. ## Check yourself The answer's key points as multiple-choice questions, with the correct option and why. 1. What does the rebound number of a Schmidt hammer mainly depend on? A. Density of the steel reinforcement B. Surface hardness of the concrete, which is related to strength C. Water-cement ratio measured inside the core D. Thickness of the member only Answer: B. The rebound of the spring-loaded mass depends on the surface hardness, which is correlated with strength. (Key point: Rebound hammer principle) 2. How many readings are taken and how are they treated in the rebound hammer test? A. One reading at the centre of the member B. At least 3 readings at the same point, take the highest C. At least 12 readings; reject those differing from the mean by more than 6 units and average the rest D. At least 12 readings, take the maximum value Answer: C. At least 12 readings 20 to 50 mm apart are taken, outliers beyond 6 units from the mean are rejected and the rest averaged. (Key point: Rebound hammer readings) 3. Which spots should be avoided? A. Smooth dry surfaces B. Surfaces ground smooth C. Middle of thick members D. Edges, honeycombed areas and over reinforcement Answer: D. Edges, honeycombing and reinforcement give wrong readings. (Key point: Precautions) 4. Why is the rebound hammer strength estimate only approximate (about ±15 to 25%)? A. It tests only the surface (about 30 mm) and is affected by carbonation, moisture, finish and aggregate B. It tests the full depth of the member but at low load C. It needs no calibration curve D. It always reads the strength of the steel bars Answer: A. Only the surface layer is tested, so surface condition and material type change the result. (Key point: Rebound hammer limits) ## Related in Concrete Technology and Masonry Structure - [UPV and rebound hammer tests](https://www.bctengineer.com/question.md?key=semester_5%2Fconcrete_technology_and_masonry_structure%3Aupv-and-rebound-hammer) — Concrete Technology and Masonry Structure, chapter 5, asked 2× - [NDT importance; Schmidt hammer test](https://www.bctengineer.com/question.md?key=semester_5%2Fconcrete_technology_and_masonry_structure%3Andt-importance-schmidt-hammer) — Concrete Technology and Masonry Structure, chapter 5 - [Importance of non-destructive testing](https://www.bctengineer.com/question.md?key=semester_5%2Fconcrete_technology_and_masonry_structure%3Andt-importance) — Concrete Technology and Masonry Structure, chapter 5, asked 4× - [Non-destructive testing methods for concrete](https://www.bctengineer.com/question.md?key=semester_5%2Fconcrete_technology_and_masonry_structure%3Andt-methods-concrete) — Concrete Technology and Masonry Structure, chapter 5, asked 4× - [Non-destructive tests for masonry](https://www.bctengineer.com/question.md?key=semester_5%2Fconcrete_technology_and_masonry_structure%3Andt-masonry-tests) — Concrete Technology and Masonry Structure, chapter 10, asked 3× - [Destructive and non-destructive tests in masonry](https://www.bctengineer.com/question.md?key=semester_5%2Fconcrete_technology_and_masonry_structure%3Adestructive-ndt-masonry-list) — Concrete Technology and Masonry Structure, chapter 10 ## Related in other subjects - [Non-destructive tests in buildings](https://www.bctengineer.com/question.md?key=semester_6%2Fbuilding_technology%3Andt-building) — Building Technology, chapter 11 - [Non-destructive tests on insulators](https://www.bctengineer.com/question.md?key=semester_8%2Fhigh_voltage_engineering%3Anon-destructive-insulator-tests) — High Voltage Engineering, chapter 7, asked 4× - [Destructive and non-destructive tests](https://www.bctengineer.com/question.md?key=semester_6%2Fbuilding_technology%3Aretrofit-destructive-tests) — Building Technology, chapter 11